Kalsinert aluminiumoksyd og ildfaste materialer

Sufficient fine grinding of the α-Al2O3 aggregates can destroy their aggregated state and make them non-porous primary crystals, at which time the particle size means close to its grain size. Activated alumina is calcined alumina that has been sufficiently finely ground and has α-Al2O3 with an original crystal size of less than 1 μm as the basic composition (20% to >90 prosent). Ved produksjon av aktivert alumina kreves det vanligvis sterk sliping, som tørrmaling i en keramisk foret kulemølle med keramiske kuler som slipemedium i mer enn 24 timer. Grunnen til at det kalles aktivert alumina betyr vanligvis at det er lett å oppnå den høyeste sintringstettheten ved sintring, men sintringstemperaturen er 100-200 grader lavere enn det lavaktive -Al2O3-pulveret; Det er lett å reagere og sintre med andre komponenter i materialmatrisen, som å kombinere med leire i matrisen for å danne mullitt, reagere med kalsiumaluminatsement for å danne CA6, reagere med MgO for å danne spinell, etc. I følge sintringsteorien , kornstørrelsen i stor grad påvirker sintringshastigheten i det innledende stadiet, det vil si dannelsen og veksten av halsen mellom kornene. Dersom kornstørrelsen reduseres til 1/10 av den opprinnelige størrelsen (f.eks. fra 5 μm til 0,5 μm), vil sintring være 1000 ganger til 10000 ganger lettere. Dette forklarer den høye termiske aktiviteten til aktivert alumina.

Maleprosessen bruker mye energi, så jo finere pulveret er, jo dyrere er det. Utseendet til silisiummikro (tåket SiO2 som genereres under produksjonen av silisiumkarbid eller silisiummetall) har i stor grad bidratt til utviklingen av lavfuktighets-, lav-sement- og ultralavt sementstøpematerialer, men denne aktive SiO2 begrenser også støpemassene. Driftstemperatur. Hvis det ikke er noen vellykket utvikling av aktivert alumina, kan den moderne ildfaste støpeindustrien ikke utvikle seg så raskt, og driftstemperaturen vil ikke overstige 1600 grader.

 Generally speaking, powders can be divided into two categories according to the shape of particle size distribution (PSD for short): one type has a unimodal PSD, that is, the particle size distribution curve only surrounds a special particle size (close to but not necessarily Yes D50) peak: the other type is the PSD with multi-peak, that is, there are two or more distribution peaks on the PSD curve. Whether it is unimodal or bimodal, generally the wider the PSD range, the greater the powder bulk density or green body density. The PSD powder with unimodal and narrow range has the lowest bulk density. Of course, activated alumina also has the above two types. The unimodal activated alumina is characterized by a higher percentage (>80 prosent) av partikler<1μm (≈primary="" crystal="" size),="" and="" thus="" has="" a="" higher="" activity,="" and="" the="" average="" value="" of="" their="" particle="" size="" (≈grain="" size)="" is="" 0.30.="" around="" 5μm.="" the="" density="" of="" this="" activated="" alumina="" green="" body="" is="" low,="" usually="" only="" 54%="" 55%="" of="" the="" theoretical="" density="" of="" α-al2o3="" (3.98g/cm3),="" but="" its="" density="" after="" firing="" at="" 15001600="" ℃="" can="" reach="" 98%="" of="" the="" theoretical="" density,="" or="" even="" higher.="" unimodal="" activated="" alumina="" is="" easily="" and="" completely="" dispersed="" in="" water="" with="" the="" aid="" of="" dispersants="" such="" as="" sodium="" polyphosphate.="" the="" content="" of="" active="" particles="" smaller="" than="" 1="" μm="" in="" the="" multi-bee="" activated="" alumina="" varies="" greatly.="" usually="" between="" 20%="" and="" 7o%.="" the="" ratio="" of="" the="" number="" of="" active="" particles="" to="" the="" number="" of="" larger="" particles="" (="">1 μm) bestemmer dens tomfyllingsevne og aktivitet. For multimodalt aktivert alumina kan mediandiameteren D50 bare representere dens finhet, snarere enn en parameter som karakteriserer dens egenskaper. Den grønne tettheten til multimodal aktivert alumina kan vanligvis nå 62 prosent 68 prosent av den teoretiske verdien, som åpenbart er høyere enn for unimodal aktivert alumina. Den sintrede tettheten som multimodalt aktivert alumina kan oppnå, avhenger av aktiviteten. Når den multimodale aluminaen med høyere aktivitet brukes til pressing og sintring, selv om sintringstemperaturen er 100-150 grader høyere enn den for den fullstendig fortettede unimodale aktiverte aluminaen, er dens sintrede tetthet bare 94 prosent og 96 prosent av den teoretiske verdien. Partiklene løsnes lett fra de større partiklene, så den multimodale aktiverte aluminaen er lett å dispergere i vann. Det brede spekteret av PSD til den multimodale aktiverte aluminaen gjør at -Al2O3-mikropulveret kan fylles inn i hullene mellom aggregatene til de ildfaste mursteinene og støpegodset og de gjenværende hulrommene mellom de store pulverpartiklene. Derfor, når det brukes i støpegods, for å oppnå samme fluiditet, kan mengden tilsatt vann reduseres med 4 prosent og 5 prosent. I matrisen til støpematerialet fungerer den multimodale aktiverte aluminaen som et smøremiddel mellom de store partiklene, noe som kan minimere løsnelsen av støpematerialet, selv når det utsettes for intensiv blanding eller pumping. holdes adskilt fra hverandre.